15.7Mo ( 632 ) Cold Rolled Stainless Steel Strip Coil PH15-7Mo
Precipitation Hardenable (PH) stainless steels are those with the highest mechanical strength among
stainless steels, associated with high corrosion resistance (similar to that presented by Austenitic 304).
The hardening mechanism in these steels is similar to the hardening mechanism of some Aluminum and Nickel alloys – aging.
PH15-7Mo is a kind of austenite precipitation hardening stainless steel.
Material PH15-7Mo in solid solution condition has good ductility, which can be deformed easily.
The material 15.7Mo in the precipitation hardened condition, is strengthened by precipitating second
precipitation phase, so the material grade PH15-7Mo in precipitation hardened condition has high strength,
high hardness, and has tolerable ductility.
| AISI / ASTM | EN / DIN | GB |
| PH15-7Mo, 632, S15700 | 1.4574, X7CrNiMoAl15-7 | 07Cr15Ni7Mo2Al |
Chemical composition %
| C | Si | Mn | P | S | Cr | Ni | Mo | Al |
| 0.09 max. | 1.00 max. | 1.00 max. | 0.040 max. | 0.040 max. | 14.00~16.00 | 6.50~7.75 | 2.00~3.00 | 0.75~1.50 |
Typical mechanical properties of PH15-7Mo
| | Solid solution condition | Precipitation hardened condition |
| Tensile Strength Rm | 850 MPa (123.25 ksi) | 1600MPa(232 ksi) |
| yield strength Rp0.2 | 420 MPa (60.9 ksi) | 1450MPa(210.25 ksi) |
| Elongation | 40% | 15% |
| Hardness HV | 225 | 480 |
Form of supply
PH15-7Mo ( 632 ) stainless steel sheet, precision strip, coil
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com