Incoloy Alloy A286 Wire UNS S66286 W.Nr 1.4980 Alloy 660 Stainless Steel Wire, Bar
A precipitation hardening stainless steel, 660 (SUH 660, UNS S66286) maintains superior strength
at high temperatures up to 700℃, surpassing austenitic stainless steels.
With a higher nickel content than Type 304, stainless 660 also includes such elements as titanium
and aluminum for hardening.
Age hardening is used to precipitate γ' phase [Ni3 (Al, Ti)] making this an extraordinarily strong metal at high temperatures.
660 is a precipitation hardening alloy.
Its strength is increased through aging after solution heat treatment.
Two stages of heat treatment are generally carried out, as follows:
- Solution heat treatment: 980℃; oil or water cooling
- Age hardening: 720℃ × 16hr; air cooling
After solution heat treatment, either oil or water cooling is required, though air cooling is better for thinner metal.
Note that it is important to use a suitable temperature and holding time for aging to obtain the target strength.
Composition ( Nominal % )
| Grade | C | Mn | Si | Cr | Ni | Mo | V | Ti | Co | Al | B |
| Alloy A286 | 0.08 max | 2.00 max | 1.00 max | 13.50 ~ 16.00 | 24.00 ~ 27.00 | 1.00 ~ 1.50 | 0.10 ~ 0.50 | 1.90 ~ 2.35 | 1.00 max | 0.35 max | 0.003 ~ 0.010 |
We prodvide A286 stainless steel wire, rod, round bar, size range from 0.5~450mm.
Specifications:
ASTM A638, ASTM A453, Bars and Forgings- AMS 5731, AMS 5732, AMS 5734,
AMS 5735, AMS 5736, AMS 5737, Strip-AMS 5525, PWA 1029, GE B50T1181, GE B50T81,
GE C50TF78, GE C50TF27, GE C50TF20, MR0175
APPLICATIONS
- Seal rings
- Retaining rings
- Jet engine components
- Power generation components
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com